| Customization: | Available |
|---|---|
| Certification: | ISO |
| Color: | Black,Orange,Red,Yellow, Transparent |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Product Description: Our 3:1 and 4:1 double-walled pipes are meticulously crafted from a dual-layer, halogen-free, flame-retardant polyolefin, combined with a robust hot melt adhesive. The outer polyolefin layer serves as a bastion of insulation, fully halogen-free, and designed to resist flames. Meanwhile, the inner hot melt adhesive layer is expertly engineered to absorb mechanical strain and form a formidable seal. Key functionalities include sealing, waterproofing, corrosion resistance, leakage prevention, multi-strand wiring harness protection, and insulation. Primarily utilized in a variety of wiring harnesses, marine wires, and metal pipes that necessitate superior sealing, insulation, bundling, and securing. Features: The outer layer is not only flame-retardant but also resistant to ultraviolet rays and wear. Boasting a shrink ratio of 3:1, our products adhere to the highest environmental protection standards, including RoHS and REACH. Available in black, orange, red, yellow, transparent, and more custom colors.
|
Performance item
|
Instruct
|
Experiment Method
|
|
Tensile Strength
|
≥10.4MPa
|
ASTM D 2671
|
|
Elongation at break
|
≥300%
|
ASTM D 2671
|
|
Tensile strength after heat aging
|
≥8.4MPa
|
158°C x168h
|
|
Elongation at break after heat aging
|
≥100%
|
158°C x168h
|
|
Axial change rate
|
-8%~ 8%
|
ASTM D 2671
|
|
Flame retardant
|
Flame retardant VW-1 or GB2408-V0, self-extinguishing in 30 seconds
|
AMS-DTL-23053/5
|
|
Breakdown strength
|
≥15KV/mm
|
IEC 60243
|
|
Withstand voltage (rated voltage 600V)
|
2500V, 1min without breakdown
|
UL 224
|
|
Volume resistivity
|
21040.cm
|
IEC 60093
|
|
Hot melt adhesive technical instructions
|
||
|
Performance item
|
instruct
|
experiment method
|
|
Softening Point
|
85+3°C
|
ASTM E 28
|
|
Water absorption
|
≤0.2%
|
ASTM D 570
|
|
Peel strength (PE)
|
≥120N/25mm
|
ASTM D 1000
|
|
Peel strength (AL)
|
≥80N/25mm.
|
ASTM D 1000
|